Silylation of TEMPO oxidized nanocellulose from oil palm empty fruit bunch by 3-aminopropyltriethoxysilane

Silylated cellulose has been successfully synthesized using TEMPO-oxidized nanocellulose (TEMPO-NC) from oil palm empty fruit bunch and 3-aminopropyltriethoxysilane (APS) in an ethanol/water medium at a low curing temperature of 40 degrees C as compared to those reported in the literature of above 100 degrees C. Confirmation of the grafting process can be seen from the new FTIR peaks at 810 cm(-1) and 749 cm(-1) which are attributed to the Si-C stretching and Si-C, and new C-13 NMR signals at 10.3, 21.7 and 42.7 ppm which are assigned to C7, C8, and C9 of the silylated TEMPO-NC. The decrease in the intensities of the cellulose peaks of C2, C3, C6 and C6' in the C-13 NMR indicates that silylation not only occurs on the hydroxyls, but more importantly on the TEMPO-NC carboxylic moiety of C6', which is postulated as being the primary factor for this successful modification. This is further corroborated by the emergence of three signals at 43, 61, and 69 ppm in the Si-29 NMR spectrum which corresponds to Si(OSi)(OR)(2)R', Si(OSi)(2)(OR)R', and Si(OSi)(3)R' units respectively. Additional evidence is provided by the EDX which shows an increase in Si weight percent of 1.94 after reaction. This silylated cellulose from OPEFB has the potentials to be used as bionanocomposite reinforcing elements. (C) 2019 Elsevier B.V. All rights reserved.